Bodies and glazes of tiles from the Ilkhanid period found at the UNESCO World Heritage site of Takht-e Soleyman were studied to identify materials and certain technical characteristics of the architectural ceramics as part of a larger project to establish different productions. In addition, ceramic vessels and technical ceramics excavated at the site were analysed for comparison. µXRF, SEM/EDX, and Raman spectroscopy were used for the material investigations. Qualitative non-invasive µXRF results allowed for categorisation of the glazes and ceramic bodies based on their overall composition. Quantitative analysis by SEM/EDX on a subset of the samples delivered detailed results on the bodies and glazes. Tiles, made from clay or stonepaste, were almost exclusively decorated with a mixed alkaline lead glaze. The PbO content of this type of glaze ranged from 8 wt% to 25 wt%. The clay bodies of some tiles corresponded to the material of the locally used kiln furniture. Moreover, glaze residues preserved on the kiln furniture proved to be from a mixed lead alkaline glaze with a PbO content of 15 wt% to 25 wt%, a composition that is comparable to the tiles’ glazes. For more insights into the local or regional production of the tiles, supplementary in-depth studies including petrographic analysis would be needed to confirm and further specify the results.