dc.description
0\. Titelblatt und Inhaltsverzeichnis 1
1\. Einleitung 4
2\. Schrifttum 5
3\. Material und Methode 20
4\. Materialen 30
5\. Ergebnisse 36
6\. Diskussion 59
7\. Zusammenfassung 66
8\. Literatur 69
9\. Anhang 76
10\. Danksagung und Lebenslauf 84
dc.description.abstract
Seit etwa 50 Jahren werden Kompositmaterialien zur Verblendung von
prothetischen Arbeiten verwendet. Verfärbungen treten regelmäßig bei der
Verwendung von Verblend-materialien auf, besonders bei
Kunststoffverblendmaterialien. Ziel dieser Studie war es, die Verfärbung von
fünf verschiedenen lichthärtenden Komposit-materialien nach Lagerung bis zu
vier Wochen in sieben verschiedenen verfärbenden Substanzen, die aus dem
alltäglichen Gebrauch stammen oder in Nahrungsmitteln enthalten sind, zu
untersuchen. Die gemessenen lichthärtenden Verblendkunststoffe waren
Compoplus, Artglass, Targis, Dentacolor und Solidex. Als verfärbende
Flüssigkeiten wurden löslicher Kaffee, Filterkaffee, Schwarzer Tee,
Chlorhexidin und Rotwein als hydrophile und Sesamöl als hydrophobe Substanz
verwendet. Die Proben wurden ebenfalls nach Lagerung in destilliertem Wasser
als Kontrollgruppe untersucht. Dabei wurde den Verhältnissen in der Mundhöhle
nur durch die Temperatur von 35 °C und dem wässrigen Medium entsprochen. Die
verwendeten Prüfkörper der Farbe A3, entsprechend der Vita-Farbskala, welche
einen Durchmesser von 20 mm und eine Dicke von 2 mm hatten, wurden in
getrennte Becher gegeben, die mit den verfärbenden Flüssigkeiten gefüllt waren
und in auf 35 °C temperiertem Wasser mit einer Frequenz von 1/s bewegt wurden.
Die Farbveränderung der Prüfkörper wurde 24 h nach Herstellung (Nullwert) und
zunächst nach 1 Tag, dann nach 1 Woche, 2 Wochen und 4 Wochen Lagerung in den
verfärbenden Lösungen gemessen. Im Gebrauch von Verblendmaterialien ist die
subjektive Wahrnehmung der möglichen Verfärbung der bedeutendste Parameter. In
dieser Studie sollten jedoch auch für das Auge nicht mehr sichtbare
Farbveränderungen ermittelt werden. Um vergleichbare Verfärbungs-werte von
Verblendkunststoffen nach Lagerung in verfärbenden Flüssigkeiten zu erhalten,
war es notwendig, empfindliche Messinstrumente zu benutzen. Das Minolta
Farbmessgerät kann die Verfärbung im CIE-Lab-System angeben, so dass die Werte
in Form von DE-Werten ausgedrückt werden konnten. Hierbei wurde nicht zwischen
oberflächlichen und eingelagerten Verfärbungen unterschieden. Nur die
Verfärbung der Prüfkörper wurde gemessen. Die Verfärbungen nahmen mit der
Dauer der Lagerung in den verfärbenden Lösungen zu. Dabei wurde
herausgefunden, dass Solidex die höchsten DE-Durchschnittswerte nach vier
Wochen Lagerung in den Lösungen aufwies. Dieses Ergebnis ist wohl durch die
Tatsache beeinflusst, dass sowohl löslicher Kaffee als auch Filterkaffe
überraschend hohe DE-Werte aufwiesen. Darauf folgten Artglass und Compoplus in
der Rangliste der stärksten Durchschnittsverfärbungen, welche allgemein recht
hohe Verfärbungswerte aufwiesen. Ein Vergleich zwischen den untersuchten
Verfärbungslösungen zeigte, dass sowohl löslicher Kaffee als auch Filterkaffee
die höchsten DE-Durchschnittswerte erreichten, gefolgt von Schwarzem Tee und
Rotwein. Sesamöl und destilliertes Wasser erreichten keine signifikanten
Farbunterschiede. Ein Unterschied zwischen hydrophilen und hydrophoben
Lösungen in ihrer Verfärbungsneigung konnte nicht gefunden werden.
de
dc.description.abstract
For more than 50 years resin based composites have been used to make tooth
coloured facings for fixed restorations. Discolorations appear regularly when
veneering materials are used in dental prosthetics especially composite
veneereing materials. The aim of this in vitro study was to examine the
discoloration of five different light cured composite veneering materials
after storage up to 4 weeks in seven different staining solutions which are
usually added to food or used in everydays life. The examined veneering
composites were Compoplus, Artglass, Targis, Dentacolor and Solidex. Boiled
and filtered coffee, black tea, chlorhexidin and red wine were used as
hydrophilic discoloring liquids and sesame oil as a hydrophobic substance.
Samples were also examined after incubating in destilled water as control. The
in vivo conditions of the oral cavity were only imitated by using a
temperature of 35 °C and the hydrophilic medium. The test samples in shade A3
of Vita company with a diameter of 20 mm and a height of 2 mm were put into
separate tubs which were filled with the staining solutions and put into water
tempered at 35 °C that was moved at a frequence of 1/s. The colour change of
the samples was evaluated 24 h after immersion (zero value) and after 1 day, 1
week, 2 weeks and 4 weeks of exposure to the staining solution. In everydays
use of veneered crowns and bridges the subjective perception of discoloration
is the most importand parameter. But small colour differnces not perceptible
to the human eye needed to be detected in this study. To establish comparative
discoloration values of composite materials after incubation in a staining
solution it was necessary to use sensitive instrumental methods. The Minolta
spectrophotometer was able to indicate the intensity of discoloration in the
CIE-Lab-System so that discoloration could be expressed in DE-values. It was
not differentiated between superficial and penetrating staining. Only the
colorchanges of the testchips were measured. Discoloration became more
significant with increasing time of exposure to the solutions. It was found
that Solidex had the highest DE average value after 4 weeks of storage in the
solutions. This result is by the way influenced by the fact that boiled coffee
as well as filtered coffee had surprisingly large DE values. Next in an
average DE staining ranking list were Artglass and Compoplus which had
generally high staining values. A comparison between the used staining
solutions showed that filtered coffee and boiled coffee reached the highest DE
values. They are followed by black tea and red wine. Sesame oil and destilled
water reached not the level of significance. A difference between hydrophilic
and hydrophobic staining solutions concerning their discoloration could not be
found.
en
dc.rights.uri
http://www.fu-berlin.de/sites/refubium/rechtliches/Nutzungsbedingungen
dc.subject
discoloration composite veneering materials
dc.subject.ddc
600 Technik, Medizin, angewandte Wissenschaften::610 Medizin und Gesundheit::610 Medizin und Gesundheit
dc.title
Untersuchung von Verfärbungen von fünf lichthärtenden Verblendkunststoffen
durch sieben im Alltag gebräuchliche, verfärbende Substanzen
dc.contributor.firstReferee
Professor Dr. Klaus Dermann
dc.contributor.furtherReferee
Professor Dr. Joachim Viohl
dc.date.accepted
2003-09-05
dc.date.embargoEnd
2003-08-15
dc.identifier.urn
urn:nbn:de:kobv:188-2003001773
dc.title.translated
Examination of the discoloration of five light cured veneering composites by
seven staining solutions used in everydays life
en
refubium.affiliation
Charité - Universitätsmedizin Berlin
de
refubium.mycore.fudocsId
FUDISS_thesis_000000001045
refubium.mycore.transfer
http://www.diss.fu-berlin.de/2003/177/
refubium.mycore.derivateId
FUDISS_derivate_000000001045
dcterms.accessRights.dnb
free
dcterms.accessRights.openaire
open access