Oxidation of silicon nanowires (Si NWs) is an undesirable phenomenon that has a detrimental effect on their electronic properties. To prevent oxidation of Si NWs, a deeper understanding of the oxidation reaction kinetics is necessary. In the current work, we study the oxidation kinetics of hydrogen- terminated Si NWs (H-Si NWs) as the starting surfaces for molecular functionalization of Si surfaces. H-Si NWs of 85-nm average diameter were annealed at various temperatures from 50°C to 400°C, in short-time spans ranging from 5 to 60 min. At high temperatures (T ≥ 200°C), oxidation was found to be dominated by the oxide growth site formation (made up of silicon suboxides) and subsequent silicon oxide self-limitation. Si-Si backbond oxidation and Si-H surface bond propagation dominated the process at lower temperatures (T < 200°C).